如何防止彩色鋁卷在生產(chǎn)過程中產(chǎn)生黑渣

來源:http://www.kangyanghua.com/ 發(fā)布時(shí)間:2020-12-10

大部分的鋁卷生產(chǎn)廠家采取積極的熱變形擠壓成型方法通過特定的(錐死,死,死)來獲得所需的橫截面的形狀鋁,由于外部因素的影響點(diǎn)顏色鋁輥在生產(chǎn)過程中會(huì)拖黑的缺陷,渣,所以如何解決這個(gè)問題,減少廢料,提高收益率?這里有三種方法:
  Most aluminum coil manufacturers adopt active hot deformation extrusion method to obtain the required cross-section shape of aluminum through specific (cone dead, dead, dead). Due to the influence of external factors, the spot color aluminum roll will drag black defects and slag in the production process, so how to solve this problem, reduce waste and improve the yield? Here are three methods:
  1. 生產(chǎn)過程控制
  1. Production process control
  切割彩涂鋁輥,用風(fēng)管清理彩涂鋁輥上的灰塵,減少灰塵的帶入,減少黑、渣的來源;
  Cut the color coated aluminum roller, use the air pipe to clean the dust on the color coated aluminum roller, reduce the introduction of dust, reduce the source of black and slag;
  殘余厚度要保持足夠,過薄的殘余壓力會(huì)導(dǎo)致彩涂鋁盤管在卷尾處卷入型材,造成黑、渣;
  The residual thickness should be enough, too thin residual pressure will cause the color coated aluminum coil to be drawn into the profile at the end of the coil, resulting in black and slag;
  擠出速度要有效控制,特別是擠出端部要減速,防止湍流卷入表面雜質(zhì)。
  The extrusion speed should be controlled effectively, especially the extrusion end should be decelerated to prevent turbulence from getting involved in the surface impurities.
  對(duì)生產(chǎn)的各個(gè)階段進(jìn)行清理;
  Clean up all stages of production;


  2. 設(shè)備設(shè)備調(diào)整
  2. Equipment adjustment
  如果擠壓棒不在中間,擠壓棒運(yùn)動(dòng)磨損材料膽囊,會(huì)造成材料膽囊腹部變形等缺陷;模座中心,上、下、左、右向中心,嚴(yán)禁移動(dòng)模座進(jìn)行生產(chǎn),上下錯(cuò)誤,要聯(lián)系機(jī)修進(jìn)行維護(hù);壓實(shí)餅的大小應(yīng)定期檢測和更換。壓實(shí)后的卷邊餅也會(huì)產(chǎn)生發(fā)黑、夾渣等報(bào)廢現(xiàn)象。材料膽囊使用很長一段時(shí)間,如出現(xiàn)變形,也會(huì)導(dǎo)致批量報(bào)廢,報(bào)廢生產(chǎn)很多,需要注意,新材料膽囊必須清除污垢的膀胱和膀胱拋光機(jī)安裝之前。
  If the extrusion bar is not in the middle, the movement of the extrusion bar will wear the gallbladder of the material, which will cause the abdominal deformation of the gallbladder of the material and other defects; the center of the mold base, up, down, left and right, is strictly prohibited to move the mold base for production, and the up and down errors should be contacted with the machine for maintenance; the size of the compaction cake should be regularly inspected and replaced. After compaction, the curling cake will also produce blackening, slag inclusion and other scrap phenomena. Material gallbladder used for a long time, if there is deformation, it will also lead to batch scrapping, scrapping a lot of production, it needs to be noted that the new material gallbladder must be cleaned of dirt before the installation of bladder and bladder polishing machine.
  3.調(diào)整模具設(shè)計(jì)和生產(chǎn)計(jì)劃
  3. Adjust mold design and production plan
  對(duì)于平面模具,如有必要,應(yīng)安裝導(dǎo)流板進(jìn)行導(dǎo)流,以縮小進(jìn)料口,夾緊死區(qū)。材料孔必須完全被模具分流孔包圍,對(duì)每一套模具進(jìn)行監(jiān)控比較,如分流孔太大的現(xiàn)象,不能在機(jī)器上生產(chǎn),要轉(zhuǎn)到機(jī)器上生產(chǎn)。
  For flat die, if necessary, guide plate shall be installed to guide the flow, so as to reduce the feed port and clamp the dead zone. The material hole must be completely surrounded by the mold shunting hole, and each set of mold shall be monitored and compared. If the shunting hole is too large to be produced on the machine, it shall be transferred to the machine for production.
  以上是鋁卷生產(chǎn)廠家為大家介紹的如何防止彩色鋁卷在生產(chǎn)過程中產(chǎn)生黑渣相關(guān)內(nèi)容,想要了解更多內(nèi)容,歡迎訪問網(wǎng)站:http://www.kangyanghua.com

主站蜘蛛池模板: 久久久久久国产精品无码超碰| 久久精品国内一区二区三区| 中文字幕理伦午夜福利片| 蜜臀av在线播放一区二区三区| 三年片免费观看大全有| 日本一区午夜艳熟免费| 久久精品国产亚洲avapp下载| 亚洲日韩色在线影院性色| 色综合久久久无码中文字幕 | 豪妇荡乳1一5白玉兰在线看| 日本边添边摸边做边爱喷水| 久久久久亚洲av综合波多野结衣 | 亚洲欧洲∨国产一区二区三区| 无码人妻熟妇av又粗又大| 精品一区二区三区无码视频 | 五十路丰满中年熟女中出| 国产精品久久无码一区二区三区网| 久久亚洲春色中文字幕久久久| 亚洲欧美一区二区三区在线| 精品亚洲成a人在线观看| 两男吃我奶头一边一个| 亚洲精品无码日韩国产不卡av | 天天天天躁天天爱天天碰2018| 亚洲国产精品久久久久婷蜜芽 | 无码专区久久综合久中文字幕| 苍井空一区二区波多野结衣av| 亚洲人精品亚洲人成在线| 精品一区二区三区自拍图片区| 久久精品国产亚洲av香蕉| 人妻大战黑人白浆狂泄| 国产情侣疯狂作爱系列| 国内精品伊人久久久久777| 无码一区二区三区在线| 粗一硬一长一进一爽一a级| 久久久国产精品| 国产精品一区二区av| 国产二区交换配乱婬| 国产伦精品一区二区三区免费| 亚洲一区av无码少妇电影| 亚洲av无码xxx麻豆艾秋| 久久精品无码一区二区三区|