導致鋁卷上色后色淺的幾個原因

來源:http://www.kangyanghua.com/ 發布時間:2022-12-29

著色后的鋁卷產品不但可以保持板材本身的性能,而且還具備更好的美觀性與裝飾性能,因此應用也是非常廣泛的,不過并不是所有的著色工藝都能得到理想的效果,有時候也會出現色淺的問題,為什么會這樣呢?下面鋁卷生產廠家來為大家分析一下吧。
Colored aluminum coil products can not only maintain the excellent performance of the plate itself, but also have better aesthetic and decorative properties, so they are also widely used. However, not all coloring processes can achieve ideal results, and sometimes the problem of light color occurs. Why is this so? Next, the aluminum coil manufacturer will analyze it for you.
1、染液溫度或濃度不均。引入攪拌工藝,同時增加攪拌的次數。
1. The temperature or concentration of dye solution is uneven. The mixing process is introduced and the mixing times are increased.
2、染液溫度太低。可給染液加溫至60℃左右。
2. The temperature of dye solution is too low. The dye solution can be heated to about 60 ℃.
3、導電不良。可能掛具松動造成的,只要注意掛緊就可避免此類問題。
3. Poor conductivity. It may be caused by loose slings, and such problems can be avoided by paying attention to fastening.
4、染料溶解不當或有不溶染料飄浮,此時易產生色差。解決的辦法是改進染料溶解。
4. If the dye is not dissolved properly or there is insoluble dye floating, color difference may occur. The solution is to improve the dye dissolution.
5、鋁卷的氧化皮膜厚度不均。可能原因是陽極氧化槽液溫度、濃度不均,這時應對槽液進行壓縮空氣攪拌,以解決此類問題。
5. The oxide film thickness of aluminum coil is uneven. The possible reason is that the temperature and concentration of anodizing bath solution are uneven. At this time, the bath solution should be stirred with compressed air to solve this problem.

鋁卷生產廠家
6、染色速度過快。工件底部入染液中而離開染液,因此底部易染深。解決的辦法是調稀染料,適當延長染色時間。
6. The dyeing speed is too fast. The bottom of the workpiece enters the dye solution first and leaves the dye solution, so the bottom is easy to dye deeply. The solution is to dilute the dye and extend the dyeing time appropriately.
7、染料太稀,可添加染料,提高濃度。
7. If the dye is too thin, add dye to increase the concentration.
以上是鋁卷上色后色淺原因的分析,希望可以對您有所幫助。我公司是專注鋁制品生產廠家,產品包括鋁皮、鋁卷等等,種類多樣,尺寸齊全,質量有保證,價格合理,如果您有相關需要的話,可以致電我公司http://www.kangyanghua.com進行咨詢訂購。
The above is an analysis of the reasons for the light color of the aluminum coil after coloring, and I hope it can be helpful to you. Our company is a manufacturer specializing in aluminum products, including aluminum sheets, aluminum coils, etc., with various types, complete sizes, guaranteed quality and reasonable prices. If you have any related needs, you can call our company http://www.kangyanghua.com Make a consultation order.

主站蜘蛛池模板: 两个人的www免费视频| 日本高清www色视频| 国产品无码一区二区三区在线| 亚洲欲色欲香天天综合网| 人人妻人人澡人人爽| 巨大黑人极品videos精品| 夜夜欢天天干| 狠狠色噜噜狠狠狠8888米奇| 亚洲色无码国产精品网站可下载 | 国产在线视频www色| 色综合 图片区 小说区| 久久精品午夜一区二区福利 | 午夜dv内射一区二区| 亚洲 欧美 清纯 校园 另类| 日韩午夜理论免费tv影院| 国产高清自产拍av在线| 亚洲av第一网站久章草| 国产精品一区二区av麻豆| 人妻精品久久久久中文字幕69| 亚洲av无码乱码在线观看| 日韩一区二区在线观看视频 | 国产精品原创巨作av女教师| 亚洲av无码欧洲av无码网站| 无码粉嫩虎白一线天在线观看 | 亚洲一区爱区精品无码| 日韩人妻无码专区精品| 琪琪色原网站在线观看| 少妇人妻大乳在线视频| 国产成人无码区免费内射一片色欲| 中国a级毛片免费观看| 精品国精品国产自在久国产应用| 精品久久久久久久免费人妻| 欧美日韩国产一区二区三区不卡| 国产乱人伦av在线无码| 无码高潮少妇毛多水多水| 人妻激情另类乱人伦人妻| 后入内射国产一区二区| 一区二区三区在线 | 欧| 无码精品一区二区三区免费视频| 亚洲精品成a人在线观看| 人妻大战黑人白浆狂泄|